B-274/AS-P108 FLAT: COATING KIT,RAIN EROSION RESISTI.
COATING KIT,RAIN EROSION RESISTI. Key specifications include specific_use: AIRCRAFT SURFACES, coloring_method: PIGMENTED, gloss_designation: FLAT, rated_drying_time: 4.000 HOURS MAXIMUM, application_method: BRUSHING AS PACKAGED OR SPRAYING AS IS OR SPRAYING AFTER THINNING, basic_formulation_type: POLYURETHANE. This part is cataloged in the U.S.
Government catalog under NSN 8010-01-520-3152, indicating validated use in U.S. government and defense logistics supply chains. Available through authorized enterprise resellers and TPM (Third Party Maintenance) channels.
Verify compatibility with your specific system configuration before ordering.
| specific_use | AIRCRAFT SURFACES |
| coloring_method | PIGMENTED |
| special_features | ANTI-STATIC TYPE; NON-MOISTURE CURING; LIMITED USE; PHOTOCHEMICALLY REACTIVE; FOR COATING EXTERIOR LAMINATED PLASTIC PARTS ON HIGH-SPEED AIRCRAFT AND MISSILES |
| gloss_designation | FLAT |
| rated_drying_time | 4.000 HOURS MAXIMUM |
| application_method | BRUSHING AS PACKAGED OR SPRAYING AS IS OR SPRAYING AFTER THINNING |
| basic_formulation_type | POLYURETHANE |
| content_within_each_unit_package | CONSISTS OF 1 GALLON OF BASE COMPONENT AND REQUIRED AMOUNT OF CATALYST, PRIMER AND PRIMER ACTIVATOR, 1 QUART OF ANTI-STATIC COATING BASE AND REQUIRED AMOUNT OF CURING AGENT, AND THINNER |
| nonvolatile_material_minimum_percentage | 45.0 |
| NSN | 8010-01-520-3152 |
| COLORING METHOD | PIGMENTED |
| RATED DRYING TIME | 4.000 HOURS MAXIMUM |
| BASIC FORMULATION TYPE | POLYURETHANE |
| CONTENT WITHIN EACH UNIT PACKAGE | CONSISTS OF 1 GALLON OF BASE COMPONENT AND REQUIRED AMOUNT OF CATALYST, PRIMER AND PRIMER ACTIVATOR, 1 QUART OF ANTI-STATIC COATING BASE AND REQUIRED AMOUNT OF CURING AGENT, AND THINNER |
| GLOSS DESIGNATION | FLAT |
| COLOR | BLACK |
| NONVOLATILE MATERIAL MINIMUM PERCENTAGE | 45.0 |
| SPECIAL FEATURES | ANTI-STATIC TYPE; NON-MOISTURE CURING; LIMITED USE; PHOTOCHEMICALLY REACTIVE; FOR COATING EXTERIOR LAMINATED PLASTIC PARTS ON HIGH-SPEED AIRCRAFT AND MISSILES |
| SPECIFIC USE | AIRCRAFT SURFACES |
| APPLICATION METHOD | BRUSHING AS PACKAGED OR SPRAYING AS IS OR SPRAYING AFTER THINNING |