PRODUCT OVERVIEW

95 A/B: COATING COMPOUND,METAL PRETREATM.

COATING COMPOUND,METAL PRETREATM. Key specifications include rated_drying_time: 6.000 HOURS MINIMUM AND 24.000 HOURS MAXIMUM, end_item_identification: F-22 AIRCRAFT, resin_component_ingredients: EPOXY RESIN, maximum_effective_time_after_mixing: 120.0 MINUTES. This part is cataloged in the U.S.

Government catalog under NSN 8030-01-497-0304, indicating validated use in U.S. government and defense logistics supply chains. Available through authorized enterprise resellers and TPM (Third Party Maintenance) channels.

Verify compatibility with your specific system configuration before ordering.

WHERE IT FITS

95 A/B

NSN: 8030-01-497-0304
FSC: 8030 — Preservative and Sealing Compounds
CAGE: 22121 — MAGNOLIA ADVANCED MATERIALS, INC. (USA)

SPECIFICATIONS

rated_drying_time	6.000 HOURS MINIMUM AND 24.000 HOURS MAXIMUM
supplementary_features	USE IN WELL VENTILATED AREA, USE IMPERVIOUS RUBBER GLOVES AND APRON, CURING PROCESS IS EXOTHERMIC, SHELF LIFE 6 MONTHS AT 80 DEGREES FAHRENHEIT OR HIGHER, 12 MONTHS AT 40 DEGREES FAHRENHEIT OR LOWER
end_item_identification	F-22 AIRCRAFT
resin_component_ingredients	EPOXY RESIN
maximum_effective_time_after_mixing	120.0 MINUTES
NSN	8030-01-497-0304

COMPONENT DIAGRAM

KEY FEATURES

•

RATED DRYING TIME: 6.000 HOURS MINIMUM AND 24.000 HOURS MAXIMUM

•

SUPPLEMENTARY FEATURES: USE IN WELL VENTILATED AREA, USE IMPERVIOUS RUBBER GLOVES AND APRON, CURING PROCESS IS EXOTHERMIC, SHELF LIFE 6 MONTHS AT 80 DEGREES FAHRENHEIT OR HIGHER, 12 MONTHS AT 40 DEGREES FAHRENHEIT OR LOWER

•

MAXIMUM EFFECTIVE TIME AFTER MIXING: 120.0 MINUTES

•

RESIN COMPONENT INGREDIENTS: EPOXY RESIN

TECHNICAL CHARACTERISTICS

RATED DRYING TIME	6.000 HOURS MINIMUM AND 24.000 HOURS MAXIMUM
SUPPLEMENTARY FEATURES	USE IN WELL VENTILATED AREA, USE IMPERVIOUS RUBBER GLOVES AND APRON, CURING PROCESS IS EXOTHERMIC, SHELF LIFE 6 MONTHS AT 80 DEGREES FAHRENHEIT OR HIGHER, 12 MONTHS AT 40 DEGREES FAHRENHEIT OR LOWER
END ITEM IDENTIFICATION	F-22 AIRCRAFT
MAXIMUM EFFECTIVE TIME AFTER MIXING	120.0 MINUTES
RESIN COMPONENT INGREDIENTS	EPOXY RESIN

OTHER ITEMS IN FSC 8030 — Preservative and Sealing Compounds

Items in the same Federal Supply class. No interchangeability or substitution relationship is implied.

8030-00-000-8225 8030-00-004-4333 8030-00-004-4334 8030-00-005-5110 8030-00-006-9391 8030-00-007-4518 8030-00-007-8333 8030-00-007-8334

SUBSTITUTES & CROSS-REFERENCES 1

5PTMKT02 TY IV GR A CL 3Same NSN cross-reference

Same NSN cross-reference

Also cataloged under this NSN

LIFECYCLE

NSN statusActive· U.S. Government catalog

HAZMAT per U.S. Government catalogDemilitarization required — mutilation + specific procedure

Ready to buy 95 A/B?

Compare prices from verified sellers on eBay

Buy on eBay →

As an eBay Partner, PartsTable may earn a commission. Your price is not affected.

FREQUENTLY ASKED QUESTIONS

What is 95 A/B?

95 A/B is a COATING COMPOUND,METAL PRETREATM.

What parts can replace 95 A/B?

There is 1 known substitute for 95 A/B: 5PTMKT02 TY IV GR A CL 3. Substitute compatibility should be verified for your specific system.

What is the NSN for 95 A/B?

95 A/B is cataloged in the U.S. Government catalog under NSN 8030-01-497-0304. This indicates validated use in U.S. government and defense supply chains.

Community Feedback

95 A/B — COATING COMPOUND,METAL PRETREATM

Request a Quote — 95 A/B